Abstract
Nanoindentation was carried out on pure tungsten carbide (WC) on the basal (0001) and prismatic (1010) planes, using Berkovich and spherical indenters, in both single load and multi-load testing. The work focuses on correlating the load-displacement curves, including elastic to plastic deformation, size effect and hysteresis with the deformation behaviour of WC. With different specimen preparation processes, the elastic to plastic deformation started at different threshold loads: This observation was found to be due to the variation in surface dislocation density. Staircase deformation was observed thought to be caused by dislocation motion and the formation of slip bands; sudden displacement discontinuities in the load-displacement response - associated with dislocation loop nucleation - occurred at, or near the theoretical shear strength. Furthermore, discontinuities in load-displacement curves were also used to confirm that hysteresis loops were a result of plastic deformation, as they when the loading was purely elastic.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.