Abstract
The research on hot deformation including flow behavior, microstructure evolution via EBSD method and the constitutive characteristic model of hot extruded GH738 alloy fabricated by spray forming was conducted by using Gleeble-3500TM simulator at the temperature range of 950~1150 ℃, strain rate range of 0.001~1 s–1 and engineering strain of 50%. The results show that the flow stress decreases with increasing of the deformation temperature and decreasing of the strain rate. The peak flow stress of coarse grain GH738 is higher than that of fine grain within the extruded GH738 alloy. The activation energy Q of extruded GH738 alloy is 651.08 kJ·mol–1. The hot deformation activation energy Q of GH738 alloy is tending to increasing with the decreasing of the original average grain size. The microstructure evolutes from original stretched grain to equiaxed grain with the increasing deformation temperature through the onset of recrystallization. The full dynamic recrystallization microstructure is obtained at the temperature above 1000 ℃ and the microstructure tend to coarsen with the higher deformation temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.