Abstract
The deformation behavior, microstructure, phase composition, and mechanical and functional properties of Ti-50.9 at.%Ni shape memory alloy during uniaxial compression in the temperature range from 25°C to 1000°C have been analyzed and are discussed herein. It was found that the deformation temperature of 300°C marked a boundary for the transition from the low- to high-temperature type of flow curves; achievement of the steady-state deformation stage was observed across a wide range of deformation temperatures. Following comprehensive analysis of the obtained data, the temperature ranges of the dynamic processes of recovery, polygonization, and recrystallization of the Ti-50.9 at.%Ni alloy were determined. Deformation in the range of dynamic polygonization is accompanied by not only the formation of B2-austenite and R-phase, but also the precipitation of fine Ti3Ni4 particles during deformational aging. The highest shape recovery characteristics were obtained after deformation of the Ti-50.9 at.%Ni alloy in the temperature range from 300°C to 600°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.