Abstract
A pure Ni single crystal of Cube orientation (001)/[100] have been deformed by reversible cold rolling to a reduction of 98% following an initial extrusion treatment. The microstructure in the as-deformed samples and in partly recrystallized specimens have been characterized in the scanning electron microscope using electron backscattered diffraction (EBSD). Line scans along the normal direction across the sample thickness show some evidence for a macroscopic pattern of subdivision. The EBSD measurements show that the deformed sample is characterized by large jumps in orientation between alternating S and Br orientations, related by misorientation angles of 50°~60°. In part of the sample a background cumulative change in orientation is seen, though local large change in orientation are also still seen. In annealed samples it is found that the orientations of the new grains
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.