Abstract
For the first time, an effective photostimulated creation of defects is observed under selective irradiation of the undoped Gd3Ga3Al2O12 single crystal and the Ce - doped Gd3(Ga,Al)5O12 single crystal and epitaxial film in the Gd3+ - related 8S7/2 → 6IJ and 8S7/2 → 6PJ absorption bands. Defects creation processes are investigated by the thermally stimulated luminescence (TSL) method in the 4.2–500 K temperature range. The dependences of the TSL glow curve peak intensity on the irradiation photon energy, irradiation temperature, and irradiation duration are measured and analyzed. The activation energy of the TSL glow curve peaks creation is found to be about 0.02 eV. Possible mechanisms of defects creation under irradiation in the absorption bands of Gd3+ in Gd3Ga3Al2O12 and Gd3(Ga,Al)5O12:Ce are discussed.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.