Abstract
This letter reports on extended defect density reduction in m-plane (11¯00) GaN films achieved via lateral epitaxial overgrowth (LEO) by hydride vapor phase epitaxy. Several dielectric mask patterns were used to produce 10 to 100 μm-thick, partially and fully coalesced nonpolar GaN films. X-ray rocking curves indicated the films were free of wing tilt. Transmission electron microscopy showed that basal plane stacking fault (SF) and threading dislocation (TD) densities decreased from 105cm−1 and 109cm−2, respectively, less than 3×103cm−1 and ∼5×106cm−2, respectively, in the Ga-face (0001) wing of the LEO films. SFs persisted in ⟨0001⟩-oriented stripe LEO films, though TD reduction was observed in the windows and wings. Band-edge cathodoluminescence intensity increased 2 to 5 times in the wings compared to the windows depending on the stripe orientation. SFs in the low TD density wings of ⟨0001⟩-stripe films did not appear to act as nonradiative recombination centers.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.