Defect recovery in Zn after low temperature electron irradiation

Abstract

Some new experimental results for Stage I and III recovery in electron-irradiated Zn are presented. Stage I (< 20 K) is found to consist of more sub-stages than previously resolved. There is little evidence for long range migration below 20 K although the possibility cannot be ruled out. Stage III (> 70 K) exhibits several features different from those reported previously. In particular, a sub-stage centered at 140 K, thought to be dose-dependent, exhibits no observable shift. A possible explanation is suggested. Several recovery models are investigated; the totality of available results cannot readily be explained fully by either of the two currently most widelyaccepted models. Es werden neue experimentelle Ergebnisse für Erholung der Stufen I und III in elektronenbestrahltem Zn mitgeteilt. Es wird gefunden, daß Stufe I (< 20 K) aus mehr Unterstufen besteht als früher angenommen. Nur geringe Hinweise für weitreichende Verlagerungen unterhalb 20 K werden gefunden, obwohl die Möglichkeit nicht ausgeschlossen werden kann. Stufe III (> 70 K) zeigt einige Merkmale, die von den früher berichteten unterschiedlich sind. Insbesondere zeigt ein bei 140 K gelegener Subzustand, von dem angenommen wird, daß er dosisabhängig ist, keine beobachtbare Verschiebung. Eine mögliche Erklärung wird vorgeschlagen. Einige Erholungsmodelle werden untersucht. Die Gesamtheit der vorhandenen Ergebnisse läßt sich von keinem der beiden zur Zeit am verbreitetsten akzeptierten Modelle vollständig erklären.