Defect evolution and its impact on the ferromagnetism of Cu-doped ZnO nanocrystals upon thermal treatment: A positron annihilation study

Abstract

CuO/ZnO nanocomposites with 4 at. % CuO were annealed in air at various temperatures between 100 and 1200 °C to produce Cu-doped ZnO nanocrystals. X-ray diffraction shows that a CuO phase can be observed in the CuO/ZnO nanocomposites annealed at different temperatures, and the Cu-doped ZnO nanocrystals are identified to be of wurtzite structure. The main peak (101) appears at slightly lower diffraction angles with increasing annealing temperature from 400 up to 1200 °C, which confirms the successful doping of Cu into the ZnO lattice above 400 °C. Scanning electron microscopy indicates that most particles in the CuO/ZnO nanocomposites are isolated when annealing at 100–400 °C, but these particles have a tendency to form clusters or aggregates as the annealing temperature increases from 700 to 1000 °C. Positron annihilation measurements reveal a large number of vacancy defects in the interface region of the nanocomposites, and they are gradually recovered with increasing annealing temperature up to 1000 °C. Room-temperature ferromagnetism can be observed in the CuO/ZnO nanocomposites, and the magnetization decreases continuously with increasing annealing temperature. However, there may be several different origins of ferromagnetism in the CuO/ZnO nanocomposites. At low annealing temperatures, the ferromagnetism originates from the CuO nanograins, and the ferromagnetism of CuO nanograins decreases with an increase in the grain size after subsequent higher temperature annealing, which leads to the weakening of ferromagnetism in the CuO/ZnO nanocomposites. After annealing from 400 to 1000 °C, the ferromagnetism gradually vanishes. The ferromagnetism is probably induced by Cu substitution but is mediated by vacancy defects in the CuO/ZnO nanocomposites. The disappearance of ferromagnetism coincides well with the recovery of vacancy defects. It can be inferred that the ferromagnetism is mediated by vacancy defects that are distributed in the interface region.