Abstract
ABSTRACTEffects of rapid thermal processing (RTP) on SiO2/GaAs interfaces have been studied with X-ray photoelectron spectroscopy, capacitance-voltage measurements and deep-level transient spectroscopy. SiO2 films of 50, 200 and 1250 nim thickness have been deposited on GaAs. RTP has been performed at 760 and 910°C for 9 s. The rapid diffusion of Ga through the SiO2 film occurs, and the As loss and the formation of the As layer near the interface are observed. The decrease of the carrier concentration occurs in all RTP samples. Five electron traps EAI (Ec – 0.27 eV), EA2 (Ec – 0.32 eV), EA3 (Ec – 0.47 eV), EA4 (Ec – 0.58 eV) and EL2 (Ec – 0.78 eV) are produced by RTP. It is considered that the production of the trap EL2 is closely related to the Ga outdiffusion into the SiO2 film and the As indiffusion from the pile-up of elemental As near the interface. Effects of SiO2 film thickness on RTP-SiO2/GaAs are also reported.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.