Abstract
This paper investigated the influence of deep cryogenic treatments (DCT) on the tensile strength, elongation to fracture and conductivity of a deformation-processed Cu-Ni-Co-Si alloy. The tensile properties were measured using a mechanical testing machine. The conductivity was evaluated using a low-resistance tester. The microstructure and precipitated phases were analyzed using scanning electron microscopy (SEM), transmission electron microscopy (TEM), an energy dispersive spectrometer (EDS) and an X-ray diffractometer (XRD). The tensile strength, elongation to fracture and conductivity of the Cu-1.34Ni-1.02Co-0.61Si alloy before and after cold rolling at 47% reduction increased with increasing DCT time and tended to be stable at about 36 h. The microstructure became more uniform after the DCT. The grain size was refined and was smallest after DCT for 48 h. The DCT promoted the precipitation of the solid solution elements Ni, Co and Si from the Cu matrix to form many fine and evenly distributed 20–70 nm spherical second-phase particles in the grains and grain boundaries.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.