AbstractA novel composite forward osmosis (FO) membrane was fabricated by introducing a chitosan (CS) sublayer between nanofibers and polyamide (PA) layer, which was beneficial to forming thin and defect‐free PA layer and improved binding strength between substrate and the selective layer. Results exhibited low reverse salt flux (0.73 gMH) while maintained high water flux (85.4 LMH), which were better than that in other reports. In order to further improve permeability of membranes, oxidized multiwall carbon nanotubes (OMWNTs) were added into PA layer based on the optimized sublayer. The crosslinking degree of PA layer was reduced, leading to loose PA layers, which promoted the increase of water flux. After modifying, water flux reached 96.9 LMH without sacrificing salt rejection. It was worth mentioning that PAN/CS composite FO membrane, which could adjust microstructure of support layer and selective layer respectively, may provide a promising way for preparing membranes with anticipated separation performance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.