Abstract
AbstractThe novel orange‐red light‐emitting garnet‐type phosphors Li3Bi3Te2O12:xSm3+ (0.005 ≤ x ≤ 0.25) were first synthesized using the high‐temperature solid‐state reaction method. The phase structure was recorded with XRD. Raman spectroscopic analysis was conducted for the first time to extract detailed structural insights of the tellurate garnet Li3Bi3Te2O12:Sm3+. The characteristics of the obtained compounds were investigated, including particle morphology, elemental mapping, diffuse reflection spectra, excitation and emission spectra, thermal stability, chromaticity coordinates according to the Commission International del′Eclairage, and color purity. The Li3Bi3Te2O12:Sm3+ phosphor could be effectively excited by 406 nm irradiation, and four sharp peaks were presented. The dominant peaks are located at 613 and 653 nm, corresponding to the typical transition of Sm3+ ions at 4G5/2→6H7/2 and 4G5/2→6H9/2, respectively. The phosphors present a regular concentration quenching trend, with an optimum Sm3+ doping concentration of 0.02. Impressively, the product demonstrates remarkable thermal stability by maintaining an emission intensity of 93% at a working temperature of 423 K. Additionally, the thermal quenching temperature (T0.5) surpasses 480 K. The lighting performance of the white light‐emitting diode fabricated using Li3Bi3Te2O12:0.02Sm3+ phosphor has been found to be exceptional, characterized by a high color rendering index (Ra = 90) and a low correlated color temperature (CCT = 5122 K). The electroluminescent spectrum of the red light‐emitting diode device fabricated by Li3Bi3Te2O12:0.02Sm3+ overlapped well with the absorption spectra of the phytochromes, suggesting its potential for plant cultivation light source. In conclusion, considering all these photoluminescent properties mentioned above, Li3Bi3Te2O12:Sm3+ phosphor can be regarded as a promising material for daily illumination and plant cultivation LEDs.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.