Decagonal quasicrystal and related crystalline phases in Mn−Ga alloys with 52 to 63 a/o Ga

Abstract

A decagonal quasicrystal (DQC) and six related intermetallic phases with large unit cells have been found in binary Mn−Ga alloys with 52 to 63 at. pct Ga by means of transmission electron microscopy (TEM). As does the Al−Mn DQC, the Ga−Mn DQC also has a periodicity of 1.25 nm along its tenfold axis. However, its Mn content, determined by electron microprobe X-ray analysis (about 45 to 50 at. pct Mn), is much higher than that of the Al−Mn DQC (about 20 to 30 at. pct Mn). The compositions of the intermetallic phases are about 53, 56, 58, and 62 at. pct Ga, corresponding respectively to the unknown structures of MnGa (50.7 to 53.4 at. pct Ga), Mn5Ga6 (55 at pct Ga), Mn5Ga7 (57.9 at. pct Ga), and Mn3Ga5 (62.9 at. pct Ga) given in the binary Mn−Ga phase diagram (Metals Hand-book, T.B. Massalski, J.L. Murray, L.H. Benneft, and H. Baker, eds., ASM, Metals Park, OH, 1986, vol. 2, p. 1144). Their lattice types have been determined by selected area electron diffraction. The ferromagnetic Mn3Ga5 is tetragonal, a=1.25 nm and c=2.50 nm; Mn5Ga7 is orthorhombic, a=4.57 nm, b=1.25 nm, and c=1.44 nm; Mn5Ga6 has two different but closely related orthorhombic unit cells, a=1.26 nm, b=1.25 nm, and c=1.48 nm as well as a=0.77 nm, b=1.25 nm, and c=2.36 nm; MnGa also has two different and related unit cells, one orthorhombic with a=2.04 nm, b=1.25 nm, and c=1.48 nm and the other monoclinic with a=2.59 nm, b=1.25 nm, c=1.15 nm, and β≈=110 deg. All these orthorhombic phases have b=1.25 nm, being the same as the periodicity along the tenfold axis of the Ga−Mn and Al−Mn DQCs. Moreover, all these six intermetallic phases give electron diffraction patterns displaying a pseudo-tenfold distribution of strong diffraction spots and are considered to be crystalline approximants of the Ga−Mn DQC.