Abstract

The hierarchical HZSM-5 was prepared via dealumination and desilication of commercial Al-rich HZSM-5, and characterized by X-ray diffraction, 27Al magic-angle spinning nuclear magnetic resonance, inductively coupled plasma mass spectrometry, scanning electron microscope, transmission electron microscope, N2 adsorption-desorption, NH3 temperature-programmed desorption, performed thermogravimetric and Raman spectrum. The results showed that partial framework of HZSM-5 was removed after steam treatment at 0.15 MPa, 500°C for 3 h. HZSM-5 with high specific surface area and much mesoporosity was obtained by the subsequent alkaline treatment. The regulation of acid quantity was achieved by altering the concentration of alkaline. Dealumination and desilication of Al-rich HZSM-5 zeolites became more effective using a combination of steam and alkaline treatments than using alkaline treatment alone. Methanol aromatization reaction was employed to evaluate the catalytic performance of treated HZSM-5 at 0.15 MPa, 450°C and MHSV of 1.5 h–1. The results indicated that after steam treatment, HZSM-5 further treated with 0.2 mol/L NaOH exhibits the best catalytic performance: the selectivity of aromatics reached 42.1% and the lifetime of catalyst attained 212 h, which are much better than untreated HZSM-5.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.