Abstract
Polycrystalline ferrites with general formula Ni 1− x Zn x Fe 2O 4 ( x = 0, 0.2, 0.4, 0.6, 0.8, and 1.0) were prepared by oxalate precipitation method. The samples were characterized by X-ray diffraction (XRD), IR and scanning electron microscope (SEM) techniques. All compositions show cubic Spinel structure. Lattice constant increases with increase in zinc content, obeying Vegard's law. The physical densities are about 98.14% of their X-ray density. Average crystallite size lies in the range 27.59–31.49 nm. Infrared studies show two absorption bands near about 400 cm −1 and 600 cm −1 for octahedral and tetrahedral sites, respectively. The resistivity of all the samples was studied. It is observed that the resistivity of nickel–zinc ferrites prepared by oxalate precipitation method is higher than that prepared by ceramic and citrate precursor method. It is attributed to greater homogeneity and smaller grain size. Activation energy in paramagnetic region is higher than that of ferrimagnetic region.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.