Abstract
The effect of direct fluorination on DC breakdown and flashover characteristics of epoxy/Al 2 O 3 nanocomposites was investigated. Pure epoxy resin and epoxy/Al 2 O 3 nanocomposites with 1, 3 and 5 wt% mass fractions were synthesized, and direct fluorination of the samples was carried out at 55 °C for 30 min using a F 2 /N 2 mixture with 20 vol% F 2 at 0.05 MPa. Fourier transform infrared spectroscopy and atomic force microscopy show that molecular chain scission occur during direct fluorination, which may significantly suppress surface charge accumulation while incorporating Al 2 O 3 nanoparticles into epoxy may restrict surface potential decay of fluorinated epoxy resin. The trap characteristics obtained by isothermal surface potential decay show that 1 wt. % sample has deeper traps and higher trap density. DC breakdown and flashover of samples were measured to evaluate the influence of nano filling and direct fluorination on electrical performance of epoxy resin. The results show that epoxy resin with higher DC breakdown and flashover strength can be obtained by simultaneous application of nano filling and direct fluorination. Compared to un-fluorinated epoxy resin, the DC breakdown and flashover voltage of fluorinated epoxy/Al 2 O 3 nanocomposites with mass fraction of 1 wt% improved 17 and 23%, respectively.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: IEEE Transactions on Dielectrics and Electrical Insulation
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.