Abstract
Based on the existed experimental results of 304 stainless steel, the evolution of fatigue damage during the stress-controlled cyclic loading was discussed first. Then, a damage-coupled visco-plastic cyclic constitutive model was proposed in the framework of unified visco-plasticity and continuum damage mechanics to simulate the whole-life ratcheting and predict the fatigue failure life of the material presented during the uniaxial stress-controlled cyclic loading with non-zero mean stress. In the proposed model, the whole life ratcheting was described by employing a non-linear kinematic hardening rule, i.e., the Armstrong-Frederick model combined with the Ohno-Wang model I, and considering the effect of fatigue damage. The damage threshold was employed to determine the failure life of the material. The simulated whole-life ratcheting and predicted failure lives are in a fairly good agreement with the experimental ones of 304 stainless steel.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.