Abstract
The crack propagation and damage evolution in metal (Ti6Al4V)-intermetallic (Al 3Ti) laminate composites were investigated. The composites (volume fractions of Ti6Al4V: 14%, 20% and 35%) were tested under different loading directions (perpendicular and parallel directions to laminate plane), to different strains (1%, 2%, 3%) and at different strain rates (0.0001 and 800–2000 s −1). Crack densities and distributions were measured. The crack density increases with increasing strain, but decreases (at a constant strain) with increasing volume fraction of Ti6Al4V. Differences in crack propagation and damage evolution in MIL composites under quasi-static (10 −4 s −1) and dynamic (800–2000 s −1) deformation were observed. The fracture stress does not exhibit significant strain-rate sensitivity; this is indicative of the dominance of microcracking processes in determining strength. Generally, the crack density after dynamic deformation is higher than that after quasi-static deformation. This is attributed to the decreased time for crack interaction in high-strain rate deformation. The effect of crack density, as quantified by a damage parameter, on elastic modulus and stress–strain relation were calculated and compared with experimental results.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.