Abstract
Unidirectional and cross‐ply Nicalon fiber‐reinforced calcium aluminosilicate (CAS) glass‐ceramic composite specimens were subjected to tension–tension cyclic fatigue and static fatigue loadings. Microcrack densities, longitudinal Young's modulus, and major Poisson's ratio were measured at regular intervals of load cycles and load time. The matrix crack (0° plies) density and transverse crack (90° plies) density increased gradually with fatigue cycles and load time. The crack growth is environmentally driven and depends on the maximum load and time. Young's modulus and Poisson's ratio decreased gradually with fatigue cycles and load time. The saturation crack densities under fatigue loadings were found to be comparable to those under monotonic loading. A matrix crack growth limit strain exists, below which matrix cracks do not grow significantly under fatigue loading. This limit coincides with the matrix crack initiation strain. Linear correlations between crack density and moduli reductions obtained from quasi‐static data can predict the moduli reductions under cyclic loading, using experimentally measured crack densities. A logarithmic correlation can predict the Young's modulus reduction in a limited stress range. A fatigue crack growth model is proposed to explain the presence of two distinct regimes of crack growth and Young's modulus reduction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.