Abstract
High-current pulsed electron beam (HCPEB) technique was applied to induce the surface irradiation of pure molybdenum. Microstructures and damaging effect of the irradiated surface were investigated in detail by X-ray diffraction, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). After 1 pulse of HCPEB irradiation, a high level of residual stress is amassed in the irradiated surface layer, while after several pulses of irradiation, a large number of adiabatic shear bands are formed on the unmelted regions of the surface, and local cracking occurs in these regions. Microstructure observations show that scattered dislocations and large amounts of vacancy clusters are formed on the irradiated surface. The adiabatic shear bands are composed of fine recrystallized grains with an average size about 1 μm. The partial softening of the irradiated surface induced by adiabatic shear bands, and the segregation of interstitial atoms in grain boundaries are primarily responsible for the surface cracking of the material. Further, nanocrystallines (20 nm) are also formed in some melted regions of the surface.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.