Abstract
AbstractAccelerated creep or stress rupture data is used for remaining life assessment for life management studies of elevated temperature components, e.g. for reformer tubes where packed nickel catalysts are used for synthesis of hydrogen, ammonia etc. This research has become a regular task because of large range of time for failure (3 to 15 years) compared to designed life (11.4 years or 100,000 hours) and huge loss associated to damage, production and safety hazards. Utilization of appropriate inspection during plant shut down has been strategic short term life assessment. Tests have been typically done by high temperature mechanical properties, microstructure analysis and accelerated creep. Inspection of micro-cracks, hot spot formation, carburization/metal dusting for inner wall and oxidation, tube diameter increment for outer wall inspection have been traditional symptoms of expiry of tubes after service exposure. Aim of this review has been to study damage analysis of reformer tube in response to so wide time frame for failures and accidents involved, even after stipulation of designed time schedules.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.