Abstract
Palladium layer (7μm thick) was deposited on the surface of the Inconel 713 LC, Inconel 625 and CMSX 4 Ni-base superalloys by the electroplating method. Electroplated samples were annealed at 1050°C for 2h in the argon atmosphere. The aluminide coatings were deposited by the CVD method. The nonmodified aluminide coating consists of the NiAl phase. Palladium modification let to formation of the (Ni,Pd)Al phase in coatings. The palladium modified as well as nonmodified coatings were oxidized at 1100°C in the air atmosphere. For both Inconel 713 LC and CMSX 4 superalloys palladium modified coatings show better oxidation resistance than nonmodified ones. Palladium inhibits the outward diffusion of substrate elements (cobalt and chromium) during oxidation of the aluminide coating. Moreover, it stabilizes the β-NiAl phase, keeps the higher content of aluminum in the β-NiAl phase for a long time and thus increases the lifetime of the coated substrate.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.