Cyclic Fatigue Resistance of Nickel-titanium Rotary Instruments according to the Angle of File Access and Radius of Root Canal

Abstract

IntroductionThe aim of this study was to compare the influences from different access angles and curvature radii on cyclic fatigue resistance of nickel-titanium rotary files. MethodsTwo file systems (2Shape [TS; MicroMega, Besançon, France] and HyFlex CM [HCM; Coltène/Whaledent, Allstätten, Switzerland]) were used. A total of 192 instruments of TS #25/.04 (TS1), TS #25/.06 (TS2), HCM #25/.04, and HCM #25/.06 were evaluated at 3 insertion angles (0°, 10°, and 20°) and 2 radii (5 mm and 3 mm) in 16-mm stainless steel artificial canals with a 60° curvature. Cyclic fatigue resistance was determined by the number of cycles to failure (NCF) using a customized testing device. Data were analyzed statistically with the significance level established at 95%. ResultsIn the 3-mm radius canal, the instruments showed lower cyclic fatigue resistance than in the 5-mm radius canal (P < .05). HCM #25/.06 and all .04 taper instruments had a significant NCF reduction at 20° and 10° in the 3-mm radius canal (P < .05), whereas TS2 showed no significant differences. In the 5-mm radius of curvature, although .06 taper instruments had no significant NCF reduction for each angle tested, .04 taper files exhibited significant NCF reduction when tested at 20° (P < .05). Comparing the same size instruments, HCM had higher NCF than TS (P < .05). Instruments with a .04 taper exhibited higher NCF than the .06 ones with the same heat treatment (P < .05). ConclusionsAn inclined insertion into the canals decreased cyclic fatigue resistance of thermal-treated instruments with a .04 taper at all radii of curvature tested. The synergistic effect of a small radius of curvature and access angulation of heat-treated instruments decreases their fatigue resistance.