Abstract
Cyclic and static loading tests were performed on reaction-bonded silicon nitride from 1000–1400 °C in air. This porous, fine-grained material contained no glassy grain-boundary phase and exhibited no slow crack growth at room temperature. Under cyclic loading, the crack-growth behaviour at 1000 °C was similar to room-temperature results; however, at 1200 and 1400 °C crack-growth rates increased significantly. Under static loading, significant crack growth was detected at 1000 °C and increased with temperature. Most of the crack growth under cyclic loading was attributed to slow crack-growth mechanisms, but evidence of cyclic crack-growth mechanisms were also observed. Oxidation played a major role in crack-growth velocity at high temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.