Abstract
Abstract Subcritical crack growth under sustained and cyclic loads at 1400°C has been investigated in a high strength Si 3 N 4 . Two different crack growth behaviours were found in this material depending on the high temperature testing history. During short-time testing, fatigue crack growth obeyed the Paris power-law expression, and under these conditions high frequency loading markedly reduced the crack propagation rate coMPared with that under sustained load or lower frequencies. Scanning electron microscopy observation revealed that this beneficial effect of cyclic loading was associated with viscous bridging by the glass phase at the crack wake, which effectively shielded the crack tip. As the fatigue test proceeded, however, crack growth rates reduced, eventually resulting in a lack of correlation between crack growth rate and stress intensity factor, and producing no discernible effect of loading frequency. Microstructural observations revealed that during this phase cavity nucleation and growth occurred and accumulated ahead of the crack tip owing to the combined action of three time-dependent events: creep, oxidation and crystallisation of the intergranular glass phase. The observed crack growth behaviour during this stage can be explained by crack tip blunting due to cavitation and glass flow and by a reducing bonding force of the glass phase across the crack surfaces due to the combined effects of oxidation, creep and crystallisation of the intergranular glass phase.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.