Abstract
The moderate corrosion rate exhibits by Mg-RE alloys make it candidate material for biodegradable implant. Owing to the operating environment, implants are subjected to stochastic cyclic load and chemical condition. The alloys response to the subjected condition determines its degree of applicability. This work studies the cyclic deformation of newly developed Mg10GdxNd alloys both in air and under corrosive environment. The corrosion fatigue test was carried out in Ringer-Acetate solution and was evaluated using mechanical hysteresis and pH-value measurements. The microstructural changes in correlation to the deformation parameters and fracture surfaces were characterized using SEM. Results show that alloying Mg10Gd with Neodymium improved its fatigue live both in air and corrosive medium. Chilled casted Mg10Gd and Mg10GdxNd were found to undergo brittle fracture in both media. Loading in Ringer-Acetate was found to reduce the fatigue life of the investigated alloys due to the interaction of corrosion and fatigue processes on the microstructure of the alloys. EDX analysis suggests that the improved fatigue life observed on the Mg10GdxNd is connected to the new ternary Mg-Gd-Nd phase observed in the microstructure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.