Abstract
AbstractIn this study, cryogenic thermal cycling was applied to bulk glassy Zr52.5Cu17.9Al10Ni14.6Ti5 (Vitreloy 105) bending samples. After that, significantly improved plasticity and better fatigue properties at three‐point bending as well as higher impact toughness were measured in dependence of the duration and the cooling rate of the thermal cycling process. This improved material behaviour is caused by reinforced shear banding, visible in scanning electron microscopy at the side faces of the specimens after fracture. A comprehensive analysis of the fracture surfaces of both quasi‐static and cyclic bent specimens revealed intense crack propagation along major shear bands and increased fatigue fracture regions, respectively. It is supposed that there is a structural rejuvenation due to the local variations of the thermal expansion coefficients within the multicomponent alloy affecting the mechanical properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Fatigue & Fracture of Engineering Materials & Structures
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.