Abstract
This work studied cycle stability of dual-phase lithium titanate (LTO)/TiO2 nanowires as a lithium battery anode. Dual-phase LTO/TiO2 nanowires were successfully synthesized by hydrothermal method at various times lithiation of 10, 24, and 48 h at 80 °C. SEM images show that the morphology of dual-phase LTO/TiO2 is nanowires with a size around 100-200 nm in diameter. The XRD analysis result indicates nanowires main components are anatase (TiO2) and spinel Li4Ti5O12. The first discharge specific capacity of LTO/TiO2-10, LTO/TiO2-24, and LTO/TiO2-48 was 181.68, 175.29, and 154.30 mAh/g, respectively. After the rate capacity testing, the LTO/TiO2-10, LTO/TiO2-24, and LTO/TiO2-48 have been maintained at 161.25, 165.25, and 152.53 mAh/g separately. The retentions for each sample were 86.71, 92.86, and 89.79 %. Based on the results of electrochemical performance, increased LTO content helped increase samples cycle stability. However, the prolonged lithiation time also produced impurities, which reduced the cycle stability.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callMore From: Journal of Multidisciplinary Applied Natural Science
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.