Abstract
A current-perpendicular-to-plane giant magnetoresistance (CPP-GMR) spin valve using epitaxial layers of Co2FeAl0.5Si0.5 (CFAS) Heusler alloy as ferromagnetic electrodes is reported. A multilayer stack of Cr/Ag/CFAS/Ag/CFAS/Co75Fe25/Ir22Mn78/Ru was deposited on a MgO (001) single crystal substrate. Epitaxial growth of the Cr, Ag, and CFAS layers in the (001) orientation up to the top CFAS layer was confirmed. Large MR ratios of 6.9% at room temperature and 14% at 6 K were observed for the CPP-GMR device. High spin polarization of epitaxial CFAS is the possible reason for high MR ratios.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.