Abstract
The effect of the TiO2 interfacial layer on rectifying junction parameters of Ag/TiO2/n-InP/Au Schottky diodes has been investigated using current-voltage (I-V) measurements in the temperature range of 120-420 K with steps of 20 K. The barrier height is found to be 0.19 eV and 0.68 eV from current-voltage characteristics at 120 K and 420 K, respectively. At 120 K and 420 K, the ideality factor is found to be 3.52 and 1.01 for the Ag/TiO2/n-InP/Au Schottky barrier diode, respectively. These results are gained by the thermionic emission theory at room temperature. Values of series resistances gained from the Cheung-Cheung method are compared with results gained from a modified Norde method. These experimental results indicate that series resistance decreases with an increase in temperature. The current-voltage (I-V) measurements showed that the diode with the TiO2 interfacial layer gave a double Gaussian property in the examined temperature range. The Richardson constant is also calculated from a modified Richardson plot and is found to be very compatible with the theoretical value. Interface state density is also examined by using I-V characteristics.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.