Abstract
AbstractThe influence of low curing temperatures (5, 10 and 15 ± 2 °C) on the strength and durability properties of ground granulated blastfurnace slag (GGBS) and ground granulated Corex slag (GGCS) concretes was studied. A standard curing temperature of 23 ± 2 °C) was also used for comparative purposes. Test specimens were cast using 100% CEM I 52.5N (PC), and three PC/Slag (GGBS or GGCS) replacement ratios of 50/50, 65/35 and 80/20, and a w/b ratio of 0.40. The specimens were cured for 28 days by submersion in water at the respective curing temperatures and then tested for durability. Durability was assessed using oxygen permeability, water sorptivity and chloride conductivity tests. The results showed that durability of the concretes decreased as the curing temperature decreased – gas permeability and water sorptivity increased while chloride resistance decreased. It was also observed that at a given curing temperature, the slag blended concretes showed superior durability performance than the plain PC concretes.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.