Curing efficiency of dual-cure resin cement under zirconia with two different light curing units.

Abstract

Adequate polymerization is a crucial factor in obtaining optimal physical properties and a satisfying clinical performance from composite resin materials. The aim of this study was to evaluate the polymerization efficiency of dual-cure resin cement cured with two different light curing units under zirconia structures having differing thicknesses. 4 zirconia discs framework in 4 mm diameter and in 0.5 mm, 1 mm and 1.5 mm thickness were prepared using computer-aided design system. One of the 0.5 mm-thick substructures was left as mono-layered whereas others were layered with feldspathic porcelain of same thickness and ceramic samples with 4 different thicknesses (0.5, 1, 1.5 and 2.0 mm) were prepared. For each group (n=12) resin cement was light cured in polytetrafluoroethylene molds using Light Emitting Diode (LED) or Quartz-Tungsten Halogen (QHT) light curing units under each of 4 zirconia based discs (n=96). The values of depth of cure (in mm) and the Vickers Hardness Number values (VHN) were evaluated for each specimen. The use of LED curing unit produced a greater depth of cure compared to QTH under ceramic discs with 0.5 and 1 mm thickness (p<0.05).At 100μm and 300 μm depth, the LED unit produced significantly greater VHN values compared to the QTH unit (p<0.05). At 500 μm depth, the difference between the VHN values of LED and QTH groups were not statistically significant. Light curing may not result in adequate resin cement polymerization under thick zirconia structures. LED light sources should be preferred over QTH for curing dual-cure resin cements, especially for those under thicker zirconia restorations.