Abstract
Studies on the effect of cobalt of unsaturated polyester resin and the effect of treated sugar palm fibre with sodium hydroxide on single fibre strength and interfacial shear strength (IFSS) are presented in this paper. 1% of methyl ethyl ketone peroxide was used as the initiator, while cobalt of variable percentages (0.05%, 0.1%, 0.2%, 0.4 %,0.6%, 0.8% and 1%)was used as the hardener. The effects on glass transition and exothermic reaction of unsaturated polyester were studied for post curing temperature determination using differential scanning calorimetry by heating the samples at 10oC/min heating rate from 30oC to 120oC with flowing of purge nitrogen gas atmosphere . For the single fibre test and IFSS, the treatment was carried out using sodium hydroxide solution with 1% concentration for one hour soaking time. Based on the optimisation percentage of cobalt, it was found that the higher the percentage of cobalt, the faster the sample tested to gel and cured. Treated sugar palm fibre exhibited better single fibre strength and IFSS between the matrices compared to untreated fibre due to the effectiveness of the alkali treatment. This can be attributed to the rearrangement of fibrils along the direction of tensile force and the removal of the coating layer and impurities after the alkaline treatment.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.