Cuprous oxide thin film directly electrodeposited from a simple copper salt on conductive electrode for efficient oxygen evolution reaction

Abstract

Catalysts made of earth-abundant elements for water splitting have attracted increasing attention in recent years. Herein we report that inexpensive cheap copper oxide thin film material can be used as an excellent electrocatalyst precursor for the oxygen evolution reaction (OER). Cuprous oxide (Cu2O) thin films were facilely electrodeposited on conductive fluorine doped tin oxide (FTO) substrates from a simple Cu(II) salt solution under a very low applied potential (-0.17V or -0.23V). Two kinds of morphologies (dendritic branching and cluster-like) of Cu2O were obtained just by altering the deposition potentials. Both Cu2O films can be used for OER, and the dendritic branching Cu2O material exhibits better performance. Under optimal conditions, OER was achieved under an onset potential at ∼0.92V (vs. Ag/AgCl) in 0.1M borate solution at pH 9.2. A catalytic current density of ∼0.1mA/cm2 required a low overpotential of ∼430mV using the electrodeposited Cu2O material under an optimal condition. The slope of the Tafel plot is ∼59.9mV/dec and the Faradaic efficiency was close to 93%. The samples were well characterized by X-ray powder diffraction (XRD), scanning electron microscopy (SEM), and X-ray photoelectron spectroscopy (XPS).