Abstract
In the present work, enhanced L10 ordering kinetics with improved crystallographic texturing in [001] direction and high magnetic coercivity of about 6 kOe is observed in L10 ordered Fe(1-x)CuxPt films, after successive isochronal vacuum annealing of multilayer structure [(Fe(1-x)/Cux)/Pt]x10. Synchrotron grazing incidence x-ray diffraction (GIXRD) measurements, performed using area detector confirms the onset of L10 ordering at 200 °C and presence of high degree of ordering at 300 °C. In-plane and out-of-plane GIXRD measurements validates texturing of magnetic easy axis [001] in out of film plane direction. Enormous increase in magnetic coercivity is observed from MOKE measurements in L10 ordered state. Lower ordering temperature with enhance (001) texturing and high magnetic coercivity is desirable for potential device applications of FePt. Effect of Cu and annealing temperature on structural and magnetic properties is investigated systematically in Fe(1-x)CuxPt films. Structural investigation discloses that lattice distortion in L10 ordered state caused by Cu addition and high interfacial energy associated with initial multilayer structure drives faster interdiffusion. Both of these aspects collectively work for FCC to FCT transformation, hence results in enhanced kinetics and texturing effects of L10 FePt.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.