Abstract
Colloidal cesium lead halide (CsPbX3, X = Cl, Br, and I) perovskite nanocrystals (NCs) demonstrate supreme optical properties in the spectra region of infrared, red, and green. High-performance blue-emitting counterparts are still eagerly required for next-generation full-color displays. However, it is challenging to obtain efficient blue perovskite NCs, especially in a deep blue region with an emission wavelength of around 460 nm or shorter. Herein, calcium halide and ammonium ions are applied simultaneously to modify the CsPb(Br/Cl)3 NCs in situ to reduce surface defects, finally remarkably enhancing the photoluminescence quantum yield (PLQY) from 13% to 93% with an emission peak at 455 nm and the Commission Internationale de l’Eclairage (CIE) coordinates at (0.147, 0.030), which is close to the requirement of the Rec.2020 standard and also meets the requirement of blue emission in DCI-P3. Bright white emission and a wide color gamut are also achieved by combining the commercial red-emitting and green-emitting phosphors. The combination of time-resolved PL spectra and femtosecond transient absorption results discloses the reason for PLQY improvement as suppressing the nonradiative recombination.
Published Version (
Free)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.