Abstract
The anion-deficient perovskite Y 0.8Sr 2.2Mn 2GaO 8−δ (where δ∼0.1) has been synthesised and the crystal and magnetic structures determined by Rietveld analysis of neutron powder diffraction (NPD) data. The material has body-centred tetragonal symmetry (I4/mmm, a=7.6373(3) Å and c=15.6636(10) Å) and consists of alternating layers of octahedral and tetrahedral polyhedra, the layers being perpendicular to [001]. The octahedral layers are preferentially occupied by manganese and the tetrahedral layers are a mixture of manganese and gallium. The precise cation distribution depends critically on preparative conditions. An unusual structural feature of these materials is the arrangement of oxygen vacancies in the tetrahedral layers: in the basic structure, isolated squares of corner-linked tetrahedra are formed instead of the chains that are observed in brownmillerite phases. Additional oxide ions in this layer probably allow the Mn ions to achieve distorted square pyramidal coordination. Low temperature NPD and magnetisation data indicate antiferromagnetic ordering below 100 K.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.