Abstract
ABSTRACTBlends of poly (ethylene terephthalate), or PET, and polycarbonate (PC) over a range of compositions were studied in isothermal crystallizations from the melt using differential scanning calorimetry (DSC). Both crystallization rate and degree of crystallinity of PET depend on blend composition. The glass transition temperature, Tg, of PET and PC in blends and pure polymer were also measured by DSC. Elevation of the Tg of PET and depression of the Tg of PC are observed upon blending. In cooling scans, dynamic crystallization from the melt was observed. In PET/PC blends with high PC content, a novel dual-peak crystallization of PET was observed. The effects of thermal history on crystallization kinetics and degree of crystallinity were also determined in isothermal crystallization studies. For Melt processing times between 1 and 30 Min and for processing temperatures between 280 and 300 °C, Melt processing temperature was seen to have a stronger effect than processing time.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call