Abstract
The crystallization of amorphous Zr 54Cu 46 alloy was investigated by using X-ray diffraction (XRD), differential scanning calorimetry (DSC) and transmission electron microscopy (TEM) techniques. The experimental results show that an endothermic peak in DSC traces for amorphous Zr 54Cu 46 alloy exists at about 1006 K, indicating following eutectoid reaction occurs, namely, Cu 10Zr 7+CuZr 2↔CuZr in amorphous Zr 54Cu 46 alloy during heating. With increasing the heating rate, the glass transition temperature T g and onset crystallization temperature T x of amorphous Zr 54Cu 46 alloy increase in parallel, and the supercooled liquid region ΔT x (= T x− T g) holds almost constant with an average value of 44 K. Both XRD and TEM results prove that Cu 10Zr 7 and CuZr 2 are main crystallization products for amorphous Zr 54Cu 46 alloy under continuous heating conditions. No CuZr phase is identified because of its small precipitation amount. Finally, the crystallization processes of amorphous Zr 54Cu 46 alloy were summarized.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.