Abstract
AbstractPoly(ethylene terephthalate) (PET) and poly (butylene terephthalate) have been modified by diamide units (0.1–1 mol%) in an extrusion process and the crystallization behavior studied. The diamides used were: for PET, T2T‐dimethyl (N, N′‐bis(p‐carbomethoxybenzoyl)ethanediamine) and for PBT, T4T‐dimethyl (N, N′‐bis(p‐carbomethoxybenzoyl)butanediamine). The above materials were compared to talc (0.5 wt%), this being a standard heterogeneous nucleator, and to diamide modified copolymers obtained by a reactor process. Two PET materials were used: a slowly crystallizing recycled grade obtained from soft drink bottles and a rapidly crystallizing injection molding grade. The crystallization was studied by differential scanning calometry (DSC) and under injection molding conditions using wedge shaped specimens; the thermal properties were studied by dynamic mechanical analysis. T2T‐dimethyl is effective in increasing the crystallization of PET in both of the extrusion compounds as well as in the reactor materials. It was also found that the crystallization temperature of poly(butylene terephthalate) could be slightly increased by the addition of nucleators.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.