Abstract
Fe-based bulk metallic glasses (BMGs) have been extensively studied due to their potential technological applications and their interesting physical and mechanical properties such as a low modulus of elasticity, high yielding stress and good magnetic properties. In the present work, the amorphous ribbon formation of Fe40Ni40B20 (numbers indicate at. %) with a ribbon form was fabricated by the single roller melt-spinning method. Rapid solidification leads to a fully amorphous structure for all compositions. The thermal properties associated with crystallization temperature of the glassy samples were measured using differential scanning calorimetry (DSC) at a heating rate of 10°C/mn. The microstructure and phase formation of the alloy have been analyzed by using X-ray diffractometry (XRD).The effect of high temperature on the isothermal crystallization of Fe40Ni40B20 ribbon was investigated by HTX-ray diffraction. In addition, these ribbon glasses also exhibit good soft magnetic properties with M-H curvature were measured under the magnetic fields between -1 kOe and 1kOe.
Highlights
Magnetic materials have undoubtedly played a central rolein the process of rapid technological innovation and evolution
The thermal properties associated with crystallization temperature of the glassy samples were measured using differential scanning calorimetry (DSC) at a heating rate of 10°C/mn
The microstructure and phase formation of the alloy have been analyzed by using X-ray diffractometry (XRD).The effect of high temperature on the isothermal crystallization of Fe40Ni40B20 ribbon was investigated by HTX-ray diffraction
Summary
Magnetic materials have undoubtedly played a central rolein the process of rapid technological innovation and evolution. The thermal properties associated with crystallization temperature of the glassy samples were measured using differential scanning calorimetry (DSC) at a heating rate of 10°C/mn. The microstructure and phase formation of the alloy have been analyzed by using X-ray diffractometry (XRD).The effect of high temperature on the isothermal crystallization of Fe40Ni40B20 ribbon was investigated by HTX-ray diffraction.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.