Abstract
Amorphous Ti 50 Ni (50-x) Cu x (at.%) (x = 15, 20 and 25) alloy ribbons were prepared by melt spinning, and then their crystallization behavior was investigated by optical microscopy, transmission electron microscopy, X-ray diffraction and differential scanning calorimetry. Wavenumber (Qp) decreased from 29.40 nm-1 to 29.29 nm-1 and ΔT(T g - T x ) increased from 31 K to 36 K with increasing Cu content from 15 at.% to 25 at.%, suggesting that glass forming ability of Ti – Ni – Cu alloy ribbons increased with increasing Cu content. Activation energy for crystallization decreased from 211.5 kJ/mol to 136.4 kJ/mol with increasing Cu content from 15 at.% to 25 at.%, suggesting that a stability of Ti – Ni – Cu amorphous decreased with increasing Cu content.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.