Abstract
Granite wastes were used as the raw materials for the preparation of CaO-MgO-Al2O3-SiO2 glass-ceramics. The waste loading was about 50.24–68.34wt% in the batch depending on the chemical compositions of glasses. Effects of SiO2/(CaO+MgO) ratio on the crystallization behavior, microstructure and properties of glass-ceramics were investigated. The results showed that the crystallization activation energy Ec increased from 322.68 to 477.10kJ/mol, and Avrami parameter n decreased from 3.78 to 2.89 as the SiO2/(CaO+MgO) ratio increase from 1.72 to 4.99, while, the crystallinity of diopside decreased gradually, and the main crystalline phase changed into armalcolite with SiO2/(CaO+MgO) ratio increase to 4.99. The increase in SiO2/(CaO+MgO) ratio lead to the decreasing in Vicker's hardness, bending strength and alkali resistance of the glass-ceramics, but improved the acid resistance.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.