Abstract
A PbTiO3/Ba0.85Sr0.15TiO3/PbTiO3 (PT/BST15/PT) sandwich thin film has been prepared on Pt/Ti/SiO2/Si substrates by an improved sol-gel technique. It is found that such films under rapid thermal annealing at 700°C crystallize more favorably with the addition of a PbTiO3 layer. They possess a pure, perovskite-phase structure with a random orientation. The polarization-electric field (P-E) hysteresis loop and current-voltage (I-V) characteristic curves reveal that a PT/BST15/PT film exhibits good ferroelectricity at room temperature. However, no sharp peak, only a weak maximum, is observed in the curves of the dielectric constant versus temperature. The dielectric constant, loss tangent, leakage current density at 20 kV/cm, remnant polarization, and coercive field of the PT/BST15/PT film are 438, 0.025, 1.3 × 10−6 Acm−2, 2.46 µCcm−2, and 41 kVcm−1, respectively, at 25°C and 10 kHz. The PT/BST15/PT film is a candidate material for high sensitivity elements for uncooled, infrared, focal plane arrays (UFPAs) to be used at near ambient temperature.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.