Abstract
This study focused on the effect of Zr-inclusion on Na[Formula: see text] conduction properties of the newly developed glass–ceramic solid solutions of Na5FeSi4[Formula: see text] and Na4ZrSi4[Formula: see text]. We experimentally confirmed formation of an all proportional solid solution in the range of [Formula: see text]= 0 and 1.0 with the composition Na[Formula: see text]Fe[Formula: see text][Formula: see text]Si4[Formula: see text]. Glass–ceramic with a fast Na[Formula: see text]-conducting Na5YSi4[Formula: see text]-type single phase was obtained in all the solid solutions. The conduction properties of the glass–ceramics were improved with increasing content of Zr, and Na4ZrSi4[Formula: see text] was the most conductive glass–ceramic. The ionic conductivities were as high as 1.9 × 10[Formula: see text] S cm[Formula: see text] and 9.3 × 10[Formula: see text] S cm[Formula: see text] at temperatures of 25∘C and 300 ∘C, respectively. The improved conductivity was attributed to the expansion of the conduction path by larger Zr ions replacing FeO6 octahedra.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.