Crystalline ha coating on peek via chemical deposition

Abstract

• Hydroxyapatite crystalline particles successfully chemically deposited on PEEK. • All process was done in room temperature and eliminates subsequent sintering. • Three dimensional porous treated layer were produced via this method. Polyether ether ketone (PEEK) has a similar elastic modulus to bone and can be a suitable alternative to metallic implants. However, PEEK is bioinert and does not integrate well with the surrounding tissues. The current commercial method for solving this problem is by coating PEEK substrates with calcium phosphates via plasma spraying. However, this method produces a low bonding strength between the substrate and the coating layer, as well as non-uniform density of the coating. In this study, chemical deposition was used to deposit HA crystalline particles on PEEK substrate without any subsequent crystallisation process therefore producing crystalline treated layer. EDX results confirmed the deposition of HA, and the XRD results confirmed that the treated layer was crystalline HA. FT-IR analysis confirmed the chemical bonding between HA and the substrate. Surface roughness increased from 24.27 nm to 34.08 nm for 3 min immersion time. The water contact angle showed an increase in wettability of the treated sample from 71.6 to 36.4 degrees, which in turn increased its bioactivity. The proposed method is a suitable alternative to other conventional methods as high temperature was not involved in the process which could damage the surface of the substrate.