Abstract
In this work, five branched polyethylenes with different branching units were synthesized using bidentate nickel (II) catalyst containing α-diimine ligands. For comparison, one linear polyethylene was also prepared using tridentate iron (II) catalyst containing α-diimine ligand. The crystalline structure of the polyethylenes was investigated using X-ray diffraction (XRD) and polarized optical microscope. The crystalline properties were also measured by differential scanning calorimeter (DSC). Viscoelastic properties of the polyethylenes were investigated using rheometric dynamic analyzer. The DSC and XRD results showed that highly branched polyethylenes exhibit no melting points and no predominating crystalline forms, while the linear polyethylene exhibits clear orthorhombic (110) and (200) reflections on XRD pattern and a clear melting point at 118 °C. The viscoelastic properties of the branched polyethylenes were very complicated due to the combined effect of the molecular weight difference and the degree of chain branching as well as the branching structure.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a call