Abstract
AbstractFor the first time AgTa0.38Nb0.62O3 (ATN) films have been grown on the La0.7Sr0.3CoO3 (LSCO)/LaAlO3 single crystal as well as onto Pt80Ir20 (PtIr) polycrystalline substrate. Comprehensive X-ray diffraction analyses reveal epitaxial quality of ATN and LSCO films on the LaAlO3(001) substrate, while ATN/PtIr films have been found to be (001) preferentially oriented. Dielectric spectroscopy performed for ATN films and bulk ceramics in a wide temperature range 77 to 420 K shows the structural monoclinic M1-to-monoclinic M2 phase transition occurs in films at the temperature 60 °C lower than in ceramics. The tracing of the ferroelectric hysteresis P-E loops indicates the ferroelectric state in ATN films at temperatures below 125 K and yields remnant polarization of 0.4 μC/cm2 @ 77 K. Weak frequency dispersion, high temperature stability of dielectric properties as well as low processing temperature of 550 °C make ATN films to be attractive for various applications.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.