Abstract
The structure of the oxygen-deficient perovskite La 0.4Sr 0.6CoO 3− δ ( δ=0.29) was investigated by transmission electron microscopy (TEM) and X-ray powder diffraction (XRD). Domains between 50 and 250 nm in size were observed in the electron microscope. Weak superstructure reflections were found with both X-ray and electron diffraction. Investigations of these superstructure reflections by selected area electron diffraction (SAED) and convergent beam electron diffraction (CBED) showed that the domains in a crystal are orientated in a 90° relationship. High-resolution transmission electron microscopy (HRTEM) images from the domain boundary also revealed a 90° orientation dependency. Using the symmetry of CBED patterns, the point group 4/ mmm was determined. By comparing reflections from the SAED pattern with possible reflections, the space group I4/ mmm (No. 139) could be isolated and finally the crystal structure was refined by Rietveld refinement.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.