Abstract
The low-loss Li2Mg4TiO7 dielectric ceramics were prepared by the conventional solid-state method. The relationship among sintering behavior, phase composition, microstructure and dielectric properties of Li2Mg4TiO7 ceramics was investigated. All the sintered samples exhibited the single phase with rock-salt structure belonging to Fm-3m space group. The higher Q·f values of samples above 1500°C were depending on crystal structure and phase composition. IR reflectivity spectrum indicated that the dielectric constant of Li2Mg4TiO7 was mainly affected by the polar optical phonons. Typically, the ceramics sintered at 1600°C exhibited excellent microwave dielectric properties with εr=13.43, Q·f=233,600GHz and τf=−7.24ppm/°C.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.